Romalin (Pulping) Specification
Covering of wall defects
We know that plaster walls and paint crack peel after a period of
time. These defects are covered by Pulping(Romalin) because it has
elasticity property. Greater resistance against humidity in comparison
to paint and other wall coverings.
Rapid application
Romalin can be applied very quickly and it can be said that in comparison
to paint, the rate of application is six time faster. if Pulping(Romalin)
is applied before the application of plaster, the speed of application
increases to nine time.
Uninflammable
Wash ability
Sound and heath isolation
Antistatic and doesn't absorb dust
Vast variety of color
Possibility of choosing or ordering the colors of your choice in
addition to the standard designs in our album.
Adhesively to all surface
In the normal process of covering walls, the following steps must
be followed:
Bricks - Mortar - Plaster - Paint
and in humid climates, the process is as follows:
Bricks - Cement Undercoat - Outer Layer
- Kenitex
In both of above processes, the RED
color steps can be omitted and Pulping(Romalin) can be used instead.
Capable of being repaired
One of the most important advantages of Pulping(Romalin) covering
is that damaged spots can be repaired, if as a results to moving furniture,
or for any other reason, the covering is struck and damaged, one can
easily repair the damaged spot so that it returns to its original
appearance with a few difference.
Romalin Samples
Technical and economical
characteristics Romalin
Romalin Instalation
| Romalin |
Range For Interiors |
| Packing |
In 45 - 51 kg plastic buckets |
| Consumption |
2.5 - 2.9 m² / 1.kg |
| Thickness of covering |
2 ~ 3 mm |
| Drying |
Between 16~48 hours depending on underlying surface and climatic
conditions |
| Shrinkage |
0.2 mm.~ |
| Bonding power |
Between 0.9 and 2.6 kg per cm² |
| Elasticity |
3 - 4 mm every m² |
| Tran spirant |
Water retention between 76% - 98% |
| Thermal insulation |
Coefficient of thermal conductivity 0.062 kcal/mhc° |
| Acoustic insulation |
As average 17 to 5000 Hz as 24 db |
| Fire resistance |
Uninflammable |
| Antistatic |
Prevents the dust from getting collected on the surface up
to 97.9% |
| Application |
With Plexiglas trowel |
| Composition |
Artificial fibers and minerals pulls pulp with cellulose-based
resins |